duplxe roller chain wheel sprocket tells: What is the reason for the cracks in the sprocket?

duplxe roller chain wheel sprocket tells: What is the reason for the cracks in the sprocket?

(Summary description)Sprocket cracks and cracks are caused by one or more reasons, such as improper grinding, improper heat treatment, excessive stress or material defects. Cracks and cracks can appear on the gear.

duplxe roller chain wheel sprocket tells: What is the reason for the cracks in the sprocket?

(Summary description)Sprocket cracks and cracks are caused by one or more reasons, such as improper grinding, improper heat treatment, excessive stress or material defects. Cracks and cracks can appear on the gear.

Information

Sprocket cracks and cracks are caused by one or more reasons, such as improper grinding, improper heat treatment, excessive stress or material defects. Cracks and cracks can appear on the gear. Let's follow the editor of duplxe roller chain wheel sprocket to have a simple understanding!
1. Quenching cracks
Quenching crack refers to the crack caused by excessive internal stress during the heat treatment of the gear. This kind of crack often appears during the quenching process, but it can also be caused by other reasons. Partially hardened gear tooth surfaces hardened by flame or induction hardening are more prone to this form of damage than full-profile hardened gear tooth surfaces or hardened and tempered gear tooth surfaces. Sometimes the cracks produced in the quenching process only gradually show up after a period of time or during tooth grinding.
2. Grinding cracks
Grinding cracks refer to the surface cracks of the gear teeth that are usually exposed in a somewhat regular pattern during or after the gear grinding. The cracks are short, not very deep, roughly parallel to each other, usually perpendicular to the track of the grinding wheel, or show a crack pattern. Grinding cracks will also be accompanied by grinding burns, which are easy to find after being etched with a nitrate solution.
3. Fatigue cracks
Fatigue crack refers to the zero pattern that expands under the action of repeated alternating stress or cyclic stress that is significantly lower than the tensile strength of the material. Sometimes the initial crack due to overload will grow slowly like a fatigue crack.
The above is the introduction by the editor of duplxe roller chain wheel sprocket: You can learn more about the causes of cracks and cracks in the sprocket.

Keyword:

Scan the QR code to read on your phone

DWSK SPROCKET

ADD: Shimenqiao Industrial Zone, Renqiu City, Hebei Province, China
TEL: 
0086-317-2805558
FAX: 0086-317-2805556
QQ: 1148504595
E-MAIL:
dwsk@vip.126.com

Alibaba: DongWang Sprocket

COPYRIGHT © RenQiu Dong Wang Machinery Parts Co., Ltd.         冀ICP备19028325号-1       Power by 300.cn